This study focused on iron making related information through analyzing slags and furnace wall collected from iron production site of Suryong-ri Wonmorongi, Chungju. Total Fe content of slags were from 36.98% to 44.47% and this range was general recovery rate of iron in ancient. Compounds of calcium included slags was supposed to add intentionally during smelting process as deoxidation agent in order that these helped to separate iron from impurities. Furnace wall didn't make of high alumina clay because of low Al2O3. Microstructure and main components of slags show that No. 1 to 3 slags with fayalite and wustite were products of iron ore smelting. However, No.4 slag is more likely to smelt by iron sand because of ulvospinel with TiO2 in No. 4 slag. Therefore, iron ore were not only used but iron sand in smelting and furnace wall made of general clay with low Al2O3 content in this area.