To preserve steel cultural properties on display outdoors, the surface of these relics is processed with a covering treatment, which is a typical anti-corrosion method. Since the registered cultural heritage of Korea No. 78 Locomotive at Jangdan Station of Gyeongui Line will be treated by preservation process and displayed in the open outdoor area, effective surface covering agents were selected through testing to prevent the corrosion of the locomotive. The mixed wax are based on two types of microcrystalline wax which is one of regular surface covering agents for locomotives and bee‘s wax. For the weather resistance test, 3 types of wax were applied to each specimen of the locomotive and the specimens were tested in the Xenon-Arc Accelerated Weathering Tester for 1000 hours in accordance with the ISO 4892-1981 criteria and the test results were compared. As a result, on the surface of the specimen coated with the bee's wax, a whitening event appears after 400 hours which causes aging, and the specimens coated by the microcrystalline wax showed signs of a whitening event after 800 hours. The moisture contact angle with the microcrystalline wax coating was also less than with the bee's wax. Therefore, it was found that the high temperature microcrystalline wax is the most effective coating agent in terms of weather resistance and moisture blocking capability and the high temperature microcrystalline wax was adopted for coating the surface of the locomotive.