One of resins, V-Flon is useful as a coating material because YK-D80, which is a solvent for V-Flon, is not highly volatile. However, it can not completely harden and can flow out when metal artifacts are joined and restored in the process of the treatment. Therefore, after the impregnation process in order to accelerate the hardening speed of a coating material, usually a dry oven was adopted. This study focused on finding the problems on the dry oven which is employed to increase the speed and investigating the most effective solvent and its composition by checking any change occurred depending on the concentration of solvents. Six different types of solvents were selected and samples were prepared in a manner that they were impregnated with solvents in three concentrations respectively (10%, 20%, 30%). To determine the condition of the samples, the stability evaluation was performed by measuring the change of color and the gloss, the thickness of coated layers, the corrosion after coating, the water resistance by contact angles. Through the comparative experiments between the natural drying and the artificial drying using a dry oven, it was found that when the dry oven is used, some problems are identified on the point of forming a uniform and stable layer because of the unstable data collected from the forced artificial dry. The experiments performed using 3 different concentration rates (10%, 20%, 30%) presented that in the case of 10% V-Flon in Xylene (using as a solvent), its layer was thin as well as it showed the high water-barrier property, which allows it to form the stably coated layer with the lower gloss and color change.